Specification for High Alumina Brick
Al2O3>=65% High Alumina Brick
Bulk Density:2.40kg/m3
Refractoriness:1770C(3218F)
Refractoriness under load 0.2MPa:1500C(2732F)
Index Product | LZ-48 | LZ-55 | LZ-65 | LZ-70 | LZ-75 | LZ-80 | LZ-85 | |
Al2O3 % | ≥48 | ≥55 | ≥65 | ≥70 | ≥75 | ≥80 | ≥85 | |
Fe2O3 % | ≤2.5 | ≤2.5 | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤1.8 | |
Refractoriness °C | 1760 | 1760 | 1770 | 1770 | 1770 | 1790 | 1790 | |
Apparent porosity % | ≤23 | ≤23 | ≤23 | ≤23 | ≤23 | ≤22 | ≤22 | |
Bulk density g/cm3 | 2.30 | 2.35 | 2.40 | 2.40 | 2.45 | 2.68 | 2.75 | |
Refractoriness under load 0.2MPa°C | 1420 | 1470 | 1500 | 1510 | 1520 | 1530 | 1550 | |
Cold crushing strength MPa | 45 | 45 | 50 | 60 | 60 | 70 | 70 | |
Permanent linear change % | 1500°C×2h | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 |
High Alumina Brick : the temperature of refractoriness under load is normally above 1420~1550°C , which is higher than the fireclay brick and it increases along with the AL2O3 content enhances.
For high alumina brick , the thermal Shock resistance is mainly decided by chemical contents and its mineral microstructure but its thermal shock resistant is worse than the fireclay brick. High alumina brick have very good ability of anti-acidity, anti-metal fluid corrode and anti-oxidation.
High Alumina Brick is used normally in industry furnaces such as Blast furnace, hot-blast furnace and EAF etc