Thermocouple Protection Silicon Nitride tube
1,High-density,low-expansion
2,Waterproof and airtight
3.Professional factory
Si3N4 Thermocouple Protection Silicon Nitride tube
Si3N4bondedd by adding industrial silicon paste into artificial aggregate.
Si3N4-SiC Thermocouple Protection tube Silicon nitride (Si3N4) bonded silicon carbide (SiC) material is produced by adding industrial silicon paste into artificial aggregate. Under high temperature, Si and N2 reacts with the formula of 2N2+3Si=Si3N4, Si3N4 bonded Sic material is formed by bonding SiC particles tightly. Therefore, Si3N4 bonded SiC material is an excellent refractory with the original properties of SiC. The material has quite high strength even under the temperature of 1700.C has properties of creep deformation resistance and anti-chemical erosion, and has excellent thermal conductivity and wear-resistance. Comparing with other several bonded SiC materials, Si3N4 bonded SiC material has attracted more and more attention.
Thermocouple Protection Silicon Nitride tube Product Feature
Si3N4 Bonded SiC material is mainly used in the production of aluminum, copper and zinc , as the lining material of the molten pool and electrolytic bath (reduction bath). The side lining of the reduction bath is eroding by aluminum and cryolite (used as additive), but Si3N4 bonded SiC material could not be eroded by aluminum, and do not have chemical reaction with cryolite. So this kind of material is ideal for the lining bricks of the electrolytic bath. In particular this kind of bricks have the excellent properties of high strength, abrasive resistance and nonconductive, so the copolymer (Al2O3 and Cryolite). The copolymer likes protective film to protect the working lining and improve the service life of electrolytic bath. At the same time, the Si3N4 bonded SiC bricks have lower thermal conductivity than silicon bricks, so they can reduce the thickness of the side wall or input higher power to expanse the loading capacity of the electrolytic bath, and to increase the output. Because of the high resistivity of the material, it can reduce the power consumption of the side -wall about 15%, saving energy and protecting environment.
Physical Properties of Silicon Nitride tube
Density g/cm3 | Relative density | Elastic modulus GPa |
Compression strength ratio25 | Hardness GPa |
3.26 0.02 | >99.5 | 300320 | 4050 | 16 - 20 |
Fracture toughness /MPam1/2 | Bending strength MPa | Poisson's ratio | Linear expansion coefficient 10-6K-1 | Webuller modulus |
6.09.0 | 9001000 | 0.25 | 3.13.3 | 1215 |
Thermal conductivity WmK-1 | Specific resistance ratio | Corrosion resistance | Size stability | Magnetic |
15~20 | 1018 | Excellent | Excellent | NO |